LOW SMOKE LOW HALOGEN FLAME-RETARDANT PVC COMPOUNDS FOR WIRES & CABLES
Technical Data Sheet
Standard: IEC 60502 and IEC 60332-1/60332-3
Property | Test Method | Unit | Specification | ||||
Application |
|
| Insulation | Insulation | Sheathing | Sheathing | Sheathing |
Standard |
|
| PVC/A IEC 60332-1 (C) | PVC/A IEC 60332-3 (C) | ST2 IEC 60332-3 (A) | ST2 IEC 60332-3 (A) | ST2 IEC 60332-3 (A) |
Density | ISO 1183 | g/cm3 | 1.45 ÷ 1.55 | 1.45 ÷ 1.55 | 1.45 ÷ 1.55 | 1.45 ÷ 1.55 | 1.45 ÷ 1.55 |
Hardness | ASTM D 2240 | Shore A | 88 ÷ 92 | 88 ÷ 92 | 88 ÷ 92 | 88 ÷ 92 | 88 ÷ 92 |
Tensile strength | IEC 60811-1-1 | N/mm2 | ≥ 12.5 | ≥ 12.5 | ≥ 12.5 | ≥ 12.5 | ≥ 12.5 |
Elongation | IEC 60811-1-1 | % | ≥ 150 | ≥ 150 | ≥ 150 | ≥ 150 | ≥ 150 |
Oxygen index | ASTM D2863 | % | ≥ 31 | ≥ 31 | ≥ 31 | ≥ 33 | ≥ 35 |
Smoke density (Non-flamming mode) | ASTM E662 | Dmc | ≤ 350 | ≤ 350 | ≤ 350 | ≤ 350 | ≤ 350 |
Aging condition | IEC 60811-1-2 |
| 100°C x 7D | 100°C x 7D | 100°C x 7D | 100°C x 7D | 100°C x 7D |
Tensile strength after aging |
| N/mm2 | ≥ 12.5 | ≥ 12.5 | ≥ 12.5 | ≥ 12.5 | ≥ 12.5 |
Variation |
| % | ≤ ±25 | ≤ ±25 | ≤ ±25 | ≤ ±25 | ≤ ±25 |
Elongation after aging |
| % | ≥ 150 | ≥ 150 | ≥ 150 | ≥ 150 | ≥ 150 |
Variation |
| % | ≤ ±25 | ≤ ±25 | ≤ ±25 | ≤ ±25 | ≤ ±25 |
Heat shock test 150°C x 1hr | IEC 60811-3-1 | - | No crack | No crack | No crack | No crack | No crack |
Loss of mass Aging condition | IEC 60811-3-2 | mg/cm2 | -
| -
| ≤ 1.5 100°C x 7D | ≤ 1.5 100°C x 7D | ≤ 1.5 100°C x 7D |
Volume resistivity at 27°C | ASTM D257 | Ω.cm | ≥ 1013 | ≥ 1013 | - | - | - |
Thermal stability at 200°C | IEC 60811-3-2 | min | ≥ 80 | ≥ 80 | ≥ 80 | ≥ 80 | ≥ 80 |
Low temperature test | IEC 60811-1-4 | °C | -15 | -15 | -15 | -15 | -15 |